FTC-500
|
 |
|
Composition |
water emulsion solution combined with 50% E-Caprolactam blocked MDI |
Properties |
- Provides excellent adhesive strength, tensile strength and elongation to Rubber compounds when it is applied to polyester or nylon tyre cord processing - Provides superior crosslinkable modification ability to increase adhesion strength when it is applied to epoxy, acryl and amino resins processing - Provides good stability to be applied to other compatible combined processing aids, as homogeneous non-ionic water dispersant |
Specification |
- Appearance |
: non-ionic milky white emulsion |
- Particle size |
: 2.5 micron below |
- pH (1% solution) |
: 7±1 |
- Solid content (% non-volatile) |
: 50 ±1 |
- Molecular Weight |
: 476 |
- melting point |
: 180~181℃ |
- NCO equivalent |
: 238 |
- blocked NCO content (%) |
: 17.5 |
|
Application |
useful in aqueous adhesive systems, Polyester yarns or fabrics for Tyres & Conveyor/V-Belts manufacturing process. |
Storage |
Should be stored in the airtight container at cool and dark places at room temp. |
|
 |
|
 |
FICONATE-60X
|
 |
|
Principal Properties |
- Good Chemical & Physical properties - Good Weatherability - Good Durability |
Type of resin |
- HDI Buiret (Fuction : 3Min) |
Specification |
- Appearance (visual) |
: Liquid clear |
(KSM-5000/2051) |
- Color (25℃,Gardner) |
: 1 Max |
(KSM-5000/4011) |
- NCO % |
: 8 ±0.5 |
(Re-blocking) |
- Solid (105℃x3Hrs) |
: 60 ± 2 |
(KSM-5000/2113) |
- Solvent |
: B-act/Xyl/n-BUOH |
(GC analysis) |
|
Application |
- Hardener of coating - Automotive coating - General industries coating |
Solubility |
- White spirit |
: insoluble |
- Butyl(Ethyl) acetate |
: Complete |
- Xylene, Toluene |
: Complete |
- Butyl cellosolve |
: Complete |
- Cellosolve acetate, PMA |
: Complete |
- n-BUOH, i-BUOH |
: Complete |
|
Compatibility |
- Acrylic resin (polyol) |
: Complete |
- Polyester resin (polyol) |
: Complete |
|
Packing |
- 20Kg /200Kg Iron Drum |
Storage |
― 1Year (Original packing state, room temperature) |
|
 |
|
|
|